Ultramid? 8202C HS BK-102 | PA6 | BASF

 二维码 3
Ultramid? 8202C HS BK-102 | PA6 | BASF
材料文字说明
Ultramid? 8202C HS is a heat stabilized, low viscosity, Polyamid 6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also available in pigmented versions.

Ultramid? 8202C HS is generally recommended for applications such as gears, valves, fittings, insulators, bushings, slides, window hardware, wiring devices, textile components and furniture casters.
机械性能干 / 已调节单位测试标准
拉伸模量3700 / 1360MPaISO 527-1/-2
屈服应力88 / 43MPaISO 527-1/-2
屈服伸长率4 / 22%ISO 527-1/-2
断裂标称应变7 / >50%ISO 527-1/-2
无缺口简支梁冲击强度, +23°CN / -kJ/m2ISO 179/1eU
简支梁缺口冲击强度, +23°C3.5 / -kJ/m2ISO 179/1eA
热性能干 / 已调节单位测试标准
熔融温度, 10°C/min220 / *°CISO 11357-1/-3
热变形温度, 1.80 MPa65 / *°CISO 75-1/-2
厚度为h时的燃烧性V-2 / *classIEC 60695-11-10
测试用试样的厚度0.7 / *mmIEC 60695-11-10
Yellow Card 现存Yes / *--
电性能干 / 已调节单位测试标准
体积电阻率>1E13 / -Ohm*mIEC 62631-3-1
相对漏电起痕指数- / 600-IEC 60112
其它性能干 / 已调节单位测试标准
吸水性9.3 / *%类似ISO 62
吸湿性2.6 / *%类似ISO 62
密度1130 / *kg/m3ISO 1183
试样制备条件价值单位测试标准
注塑, 熔体温度260°CISO 294
注塑, 模具温度80°CISO 294
函数
www.campusplastics.com1E11E21E31E41E11E21E3粘度-剪切速度Ultramid? 8202C HS BK-102剪切速度 in 1/s粘度 in Pa s250°C260°C270°C
www.campusplastics.com1E11E21E31E41E31E41E51E6剪切应力-剪切速度Ultramid? 8202C HS BK-102剪切速度 in 1/s剪切应力 in Pa250°C260°C270°C
www.campusplastics.com0123456020406080100120140应力-应变.Ultramid? 8202C HS BK-102 (干)应变 in %应力 in MPa-40°C23°C80°C120°C150°CB折断B
www.campusplastics.com0123456010203040应力-应变.Ultramid? 8202C HS BK-102 (湿)应变 in %应力 in MPa23°C80°C100°C120°C
www.campusplastics.com0123456010002000300040005000正割模量-应变.Ultramid? 8202C HS BK-102 (干)应变 in %正割模量 in MPa-40°C23°C80°C120°C150°CB折断B
www.campusplastics.com01234560500100015002000正割模量-应变.Ultramid? 8202C HS BK-102 (湿)应变 in %正割模量 in MPa23°C80°C100°C120°C
典型数据
加工方法
注塑
供货形式
粒料
特殊性能
经热稳处理的/耐热的


会员登录
登录
我的资料
我的收藏
留言
回到顶部
http://www.hk-topking.com http://www.rahuabei.com http://www.yesant.com http://www.feiyuzs.com http://www.shanghaihongshun.com http://www.shdtyl.com http://www.tianyagroup.com http://www.chinafwz.com http://www.0722rcw.com http://www.025mpc.com http://www.hbshenfeng.com http://www.hnchenxin.com http://www.hhys2008.com http://www.xld128.com http://www.ordiform.com http://www.ahdoos.com http://www.baigish.com http://www.goodilove.com http://www.elicenta.com http://www.sy7388.com http://www.zjxxmj.com http://www.inbascan.com http://www.0411tt.com http://www.zbboteng.com http://www.hgjjjx.com http://www.novadjs.com http://www.xm-light.cn http://www.harborcityhotel.com http://www.happytigertours.com http://www.hustcs88.com